Refractory Products
Pressed Shape
C-4

Highly refractory material used in the continuous casting process for making metal railroad wheels. It is non-wetting for ferrous metals.
Kiln Furnitures
Cast Sicterm 880

Thermal treatment furnace wall and muffle; Furniture for ceramic(sanitaryware) firing; special shapes for non-ferrous metals melting.
Pressed Shape
Condor MT-4i

Resin bonded, magnesia-carbon pressed shapes with fused grain and antioxidant additions
Kiln Furnitures
Cordierite Mix 05-04

A high strength, thermal shock resistant, pressed cordierite mix suited for kiln furniture requirements
Kiln Furnitures
Cordierite Mix 05-05

A high strength, thermal shock resistant, pressed cordierite mix suited for kiln furniture requirements
Kiln Furnitures
Cordierite Mix 05-06

A high strength, thermal shock resistant, pressed cordierite mix suited for kiln furniture requirements
Kiln Furnitures
Cordierite Mix 05-10

A high strength, thermal shock resistant, pressed cordierite mix suited for kiln furniture requirements
Kiln Furnitures
Cordierite Mix 05-12

A high strength, thermal shock resistant, pressed cordierite mix suited for kiln furniture requirements
Kiln Furnitures
Cordierite Mix 85-25

A high strength, thermal shock resistant, pressed cordierite mix suited for kiln furniture requirements
Kiln Furnitures
Cordierite Mix 93-04

A high strength, thermal shock resistant, pressed cordierite mix suited for kiln furniture requirements
Kiln Furnitures
Cordierite Mix 94-04

A high strength, thermal shock resistant, pressed cordierite mix suited for kiln furniture requirements
Kiln Furnitures
Cordierite PT-109

Applicable where high thermal shock resistance and resistance to glaze penetration are necessary at moderate temperatures. PT-109 should be used in applications where greater thermal shock resitance is required than achieved by the general use cordierite mixes.
Applicable where high thermal shock resistance and resistance to glaze penetration are necessary at moderate temperatures. PT-109 should be used in applications where greater thermal shock resitance is required than achieved by the general use cordierite mixes.
Kiln Furnitures
Cordierite PT-265A

Applicable where high thermal shock resistance and resistance to glaze penetration are necessary at moderate temperatures. 48-38 T is a good general mix which can be used for most applications where cordierite is required.
Applicable where high thermal shock resistance and resistance to glaze penetration are necessary at moderate temperatures. 48-38 T is a good general mix which can be used for most applications where cordierite is required.
Kiln Furnitures
Cordierite PT-313

This composition should be used when bot a higher use temperature and fast fire is indicated.